Single Wall, Heat Shrinkable Polyolefin Tubing |
Single Wall, Heat Shrinkable Polyolefin Tubing |
|
Environmental-friendly(Halogen Free), Flexible, Heat shrinkable Insulating polyolefin tubing (MT-ST-1)
|
Features:
1.2:1 shrink ratio (Radial change), shrink ratio in longitudinal≤5%
2.Min. shrink temperature: 80 ℃ ; Full recovery temperature: 120 ℃
3.Continuous Operating Temperature: -40 ℃ ~125 ℃
4.Specifications / Approvals: UL 224, CSA22.2
5.Flame-retardant
6.Meet ROHS(Restriction of use of certain Hazardous Substances)requirement
7.Flexible
|
Application
C-2 is recommended for all general purpose applications such as electrical insulation, color coding, cable bundling, light harness jacketing and identification of wires, cables, pipes, and electrical and electronic components, and mechanical protection where UL or CSA recognition as VW-1 rated material is desirable.
Dimension:
Size
|
As supplied
|
After Recovery(mm)
|
Standard Package
|
Inch
|
mm
|
Internal diameter(mm)
|
Internal diameter Max(mm)
|
Wall thickness (mm)
|
Spool Length m/spool
|
3/64
|
0.8
|
1.1±0.2
|
0.50
|
0.22
|
200
|
1/16
|
1.0
|
1.5±0.2
|
0.65
|
0.28
|
200
|
1.5
|
2.0±0.2
|
0.85
|
0.32
|
200
|
3/32
|
2.0
|
2.5±0.2
|
1.00
|
0.35
|
200
|
2.5
|
3.0±0.2
|
1.30
|
0.38
|
200
|
1/8
|
3.0
|
3.5±0.2
|
1.50
|
0.40
|
200
|
3.5
|
4.0±0.2
|
1.80
|
0.42
|
200
|
4.0
|
4.5±0.2
|
2.00
|
0.45
|
200
|
3/16
|
4.5
|
5.0±0.2
|
2.30
|
0.50
|
200
|
5.0
|
5.5±0.2
|
2.5
|
0.55
|
100
|
1/4
|
6.0
|
6.5±0.2
|
3.0
|
0.55
|
100
|
5/16
|
7.0
|
7.5±0.3
|
3.5
|
0.55
|
100
|
8.0
|
8.5±0.3
|
4.0
|
0.60
|
100
|
3/8
|
9.0
|
9.5±0.3
|
4.5
|
0.60
|
100
|
10.0
|
10.5±0.3
|
5.0
|
0.60
|
100
|
11.0
|
11.5±0.3
|
5.5
|
0.60
|
100
|
1/2
|
12.0
|
12.5±0.3
|
6.0
|
0.60
|
100
|
13.0
|
13.5±0.3
|
6.5
|
0.65
|
100
|
14.0
|
14.5±0.3
|
7.0
|
0.65
|
100
|
5/8
|
15.0
|
15.5±0.4
|
7.5
|
0.70
|
100
|
16.0
|
16.5±0.4
|
8.0
|
0.70
|
100
|
17.0
|
17.5±0.4
|
8.5
|
0.70
|
100
|
3/4
|
18.0
|
19.0±0.5
|
9.0
|
0.80
|
100
|
20.0
|
21.0±0.5
|
10.0
|
0.80
|
100
|
22.0
|
23.0±0.5
|
11.0
|
0.80
|
100
|
1
|
25.0
|
26.0±0.5
|
12.5
|
0.90
|
50
|
28.0
|
29.0±0.5
|
14.0
|
0.90
|
50
|
1-1/4
|
30.0
|
31.5±1.0
|
15.0
|
0.95
|
50
|
35.0
|
36.5±1.0
|
17.5
|
1.00
|
50
|
1-1/2
|
40.0
|
41.5±1.0
|
20.0
|
1.00
|
50
|
45.0
|
46.5±1.0
|
22.5
|
1.00
|
25
|
2
|
50.0
|
≥50
|
25.0
|
1.00
|
25
|
60.0
|
≥60
|
31.0
|
1.30
|
25
|
70.0
|
≥70
|
36.0
|
1.30
|
25
|
3
|
80.0
|
≥80
|
41.0
|
1.46
|
25
|
90.0
|
≥90
|
46.0
|
1.46
|
25
|
4
|
100.0
|
≥100
|
51.0
|
1.46
|
25
|
5
|
120.0
|
≥120
|
61.0
|
1.56
|
25
|
6
|
150.0
|
≥150
|
76.0
|
1.56
|
25
|
7
|
180.0
|
≥180
|
91.0
|
1.56
|
25
|
Performance:
Property
|
Test Method
|
Typical Performance
|
Tensile Strength(Mpa)
|
ASTM D2671
|
10.4MPa
|
Elongation(%)
|
ASTM D2671
|
200%
|
Tensile Strength after Heat aging
|
UL224 158℃ X168hrs
|
≥7.3
|
Elongation after aging(%)
|
UL224 158ºċ X168hrs
|
≥100
|
Heat shock
|
UL224 225ºċ X4hrs
|
No dripping No cracking
|
|
|